eSUN Bio-Resin Flexible eResin Flex
eSUN Flexible Bio-Resin / eResin have a very wide range of reactivity. UV wavelengths of up to 420nm. By incorporating a blend of photo-initiators, monomers & sensitizers, almost any UV light source can be used to initiate the polymerisation process of eSun resins.
- Suitable for most mSLA printers/ UV LCD printers.
- High Flex , no breakage after multiple folds
- High tough rating
- Better tear resistance
- Faster Printing Speed
- Low odor (Ester-like)
- Easy clean-up with isopropyl alcohol
- Comes in 500ml bottle
- Shrinkage vol: 6.9%
- Can be used in printing fields like e.g. flexible wear/shoe models/sports grip
Recommended settings are as follows/ or do follow as per manufacturer's recommendation:
- Optimal printing temperature: 25 to 35 °C
- Lift-speed: within 60mm /min
- Exposure: >10sec
- Cure: Under direct sunlight for 30min in water /or 15mins under UV LED
- The rising height is more than 8mm after exposure of each layer. The rising speed is within 60 mm/min. The waiting time between two exposure is more than 10s
Properties of Post-Cured Material (as per manufacturer's data)
|
MEASUREMENT |
TEST METHOD |
VALUE |
|
Shore A Hardness |
ASTM D 2240 |
85-90 |
|
Tensile strength MPa |
ASTM D 412 |
6-8 |
|
Elongation at break/% |
ASTM D 412 |
100-150 |
|
Tearing Strength/kN·m-1 |
ASTM D 624 |
390-420 |
|
Compression Set/% |
ASTM D 395 |
/ |
|
Proportion（H2O，25℃） |
GB/T 6750-1986 |
1.116 |